Condensation tin cure molding silicone rubber, Tin-based silicone, also called condensation-cure silicone, are two-component materials which cure at room temperature (RTV) to flexible, high tear-strength rubbers. Tin cured silicone can be poured onto models or they can be made brush-able by adding a Thixotropic additive. They are ideal for molds where easy release or high temperature resistance is required.
Hardness (shore A)
Tear strength (KN/m)
Elongation break (%)
Linear shrinkage (%)
Mixing ratio (%)
Working time (mins)
Curing time (hrs)
How to make molds
Preparing the Model
Porous surfaces, such as wood, should be dried and sealed. Also applying a release agent, such as petroleum jelly will aid in easy release of a silicone mold. Because silicone can sometimes bond to surfaces which contain silica, such as glass, cements and natural stone; it is recommended to do a spot test for possible adhesion.
This material can readily accept pigments.Stirring individual components before use is recommended. Make sure to weigh and measure accurately. Close containers tightly after use. Products should be stored in their original, sealed containers in an environment that does not exceed 90℉. Under these conditions, the product will achieve the expected shelf life.
The following procedure is an example of a 100:3 mix ratio addition cure product. Please refer to the product’s technical sheet for mix ratio information:
Mixing: Charge 100kg by weight of “Part A” and 3kg by weight of “Part B” into a clean, compatible metal or plastic container. The volume of the container should be 3-4 times the volume of the material to be mixed. This allows for expansion of the siloxane material as it de-gasses.
Mix thoroughly by hand or with mixing equipment while minimizing air entrapment until a homogeneous mixture is obtained. This will occur when the material takes on a uniform color with no visible striations. Scrape the sides and bottom of the container thoroughly several times while mixing. Once mixing is complete it is recommended that the material be de-aired 2-3 times by intermittent evacuation for a few minutes to minimize any imperfections due to bubbles in the cured material. Typically after releasing the vacuum 2-3 times the mass will collapse on itself at which time the vacuum should be left on only 2-4 minutes longer.
Dongguan Rongxin Silicone Technology CO.,Ltd
Factory add:NO.16,Tianxin Industry Zone,Tangxia,Dongguan,Guangdong Province ,China
Branch Company in Shenzhen :
Shenzhen Rongxingda Polymer Material Co.,Ltd
Office add:804Room,8F,Tianfuxing Building,Liuxian Road,Minzhi,Longhua District ,Shenzhen,China